广东体育彩票11选五

  • <tr id='xB4Wqx'><strong id='xB4Wqx'></strong><small id='xB4Wqx'></small><button id='xB4Wqx'></button><li id='xB4Wqx'><noscript id='xB4Wqx'><big id='xB4Wqx'></big><dt id='xB4Wqx'></dt></noscript></li></tr><ol id='xB4Wqx'><option id='xB4Wqx'><table id='xB4Wqx'><blockquote id='xB4Wqx'><tbody id='xB4Wqx'></tbody></blockquote></table></option></ol><u id='xB4Wqx'></u><kbd id='xB4Wqx'><kbd id='xB4Wqx'></kbd></kbd>

    <code id='xB4Wqx'><strong id='xB4Wqx'></strong></code>

    <fieldset id='xB4Wqx'></fieldset>
          <span id='xB4Wqx'></span>

              <ins id='xB4Wqx'></ins>
              <acronym id='xB4Wqx'><em id='xB4Wqx'></em><td id='xB4Wqx'><div id='xB4Wqx'></div></td></acronym><address id='xB4Wqx'><big id='xB4Wqx'><big id='xB4Wqx'></big><legend id='xB4Wqx'></legend></big></address>

              <i id='xB4Wqx'><div id='xB4Wqx'><ins id='xB4Wqx'></ins></div></i>
              <i id='xB4Wqx'></i>
            1. <dl id='xB4Wqx'></dl>
              1. <blockquote id='xB4Wqx'><q id='xB4Wqx'><noscript id='xB4Wqx'></noscript><dt id='xB4Wqx'></dt></q></blockquote><noframes id='xB4Wqx'><i id='xB4Wqx'></i>

                如何提高Ni60合金粉耐磨涂层的韧性?

                2019-11-04新闻资讯

                由于Ni60涂层的耐广东11选5开奖结果查磨性,想到用粉末冶金的方法制作涂层,就是把Ni60合金粉预涂敷在金属基体上,随后进行烧结(900℃),因为该过程中粉末是不熔化得,因而不同于堆焊广东11选五开奖结果查手机版下载和喷焊等。发现的一个主要问题是使用此方法制备的耐磨层虽然硬度能够达到HRC 60,但是韧性非常差,断口SEM发现粉末颗粒并没有广东11选五一定牛势图完全粘结在一起(如图),粉末轮廓非常明显。我想可能是烧结温度低的原因,但是它的熔点就是970℃,我不能超过它啊~~

                现在想调整粉末的成分,因为其中Si的注意用主要是降低熔点和脱氧造渣功能,而使用粉末冶金方法是不需要这个功能的,因此考虑降低Si含量甚至去掉Si。这样的话粉末熔点提高了,烧结温度也相应提高,然后粉末之间粘结得更充分。就是不知道这样会不会降低耐磨层的硬度?

                f7efefabd3eb0392836c1a5767e4d378.jpg

                设备推荐:/3c95un/product/metallurgical/

                6ea8118c9ca1ba30b13cdc4d2f772aec.jpg

                有个疑问,堆焊的方法,Ni60粉就能达到HRC60,而且用熔化的方法,与基体的结合也比较好,为什么要用烧结的方法?

                是想广东一定牛走势粉末冶金的材料组织均匀,无偏析,无热影响区。而且堆广东11选5计划推荐焊方法制备的耐磨层厚度会受限制,一般都得经过多道多次堆焊,无法保证成分和性能的均一..